Aluminum Rod Ccr Line

• Certification: CE, ISO, CE, ISO, ISO9001
• Customized: Customized
• Surface Treatment: Painted, Color Coated
• Fuel: Gas Coal Electric, Electric
• Range of Applications: Industrial, Industrial
• Type: Cusomized, Eaf
• Model NO.: ZZR 2400/9.5/+255/15 Type
• Place Style: Vertical
• Usage: Steel Molding
• Alloy: Non-Alloy
• Transport Package: Wooden Case
• Specification: ZZR 2400/9.5/+255/15
• Trademark: VILLE INDUSTRY
• Origin: China
• HS Code: 85
• Production Capacity: 500/Year

Product Description

ZZR 2400/9.5/+255/15 Type 
Aluminum Rod CCR Line 
1. Service and Performance
Aluminum rod continuous casting and rolling line can produce three kinds of conductive aluminum rods of φ15,φ13,φ9.5mm, φ15 aluminum rod is produced by 11 rolling stands, φ12 aluminum rod is produced by 13 rolling stands and φ9.5mm aluminum rod is produced by 15 rolling stands.

2. Process Flow
2.1. Aluminum ingot and scrap aluminum wire → aluminum melting furnace →aluminum holding furnace →four-wheel continuous casting machine → hauling machine → automatic shearer→ continuous rolling mill →roller leading pipe → coiler with dual basket
2.2.Melt aluminum or prepared melt aluminum is injected to six-wheel continuous casting machine through launder and is cast to aluminum bar of 2,420mm². Scrap aluminum bar is cut by oil hydraulic shearer and then acceptable aluminum bars are sent to continuous rolling mill. Conductive aluminum rods are sent to coiler 

3. Main Technical Parameters
3.1. Diameter (of finished products of conductive Aluminum rod): φ9.5 φ12 and φ15mm (as customer requested) 
3.2. Capacity : 4~4.5 t/h
3.3. Coil's weight: ~2t
3.4. Overall weight of main equipment: ~ 65t
 3.5. Overall power of main equipment: ~350kW (excluding furnace)
3.6. Finished rolling speed: ≤6.2m/s
3.7. Overall dimension: approx. 35.×7.2×4.2m (L × W × H) 
  
4. Continuous casting and rolling line introduction
4.1. Four-wheel Continuous Casting Machine (with 2pcs of casting ladles) 1 set
It adopts four-wheel continuous casting machine which is the most advanced continuous casting machine at home and abroad at present. The advantages are: 

1. The technology ensures aluminum ingots is on the center line of rolling, and replace of an angle of 22° between aluminum ingots and center line of rolling, casting ingots will be twisted, it will take bad effect on the rolling quality.  
2. It can reduce one operator of fishing flow-control and simplify the casting operating process. Automatically flow control, ensure that the casting of flow of aluminum molten is stable. Fishing flow controlling depends on the operators skills so as to the quality controlling is not stable. 
3. The horizontal pouring system can make the molten pouring stable and no bubbled, so the slag and stoma will be reduced outstandingly and improve the quality of the ingots. 
4. Dismounting the casting wheel is very convenient; the steel belts also can be adjusted during the operation. 
5. The production is available for high-end users, such as the enterprise who produce CCA wire, aluminum enameled wire, extrusion condenser pipe and aluminum flat wire, expand the use range of the production and economic efficiency.

1. Diameter of crystallizing wheel: φ1,600mm
2. Crystallizing wheel rotating speed:  1.66-3.3r/min   
3. Sectional area of crystallizing wheel: 2,400mm²
4. Ingot outlet speed:   7.8-15.6m/min  
5. Motor: 5.5 kW  n=1,500r/min  AC motor 
6. Cooling water pressure: 0.35-0.5MPa   12 passes 
7. Amount of cooling water: 100t/h (inner 60 t/h, outer 40 t/h)

I. The function and process flow of the equipment
This furnaces group is the dedicated furnaces for the 4-4.5T/h EC grade aluminum rod continuous casting and rolling line (CCR line). It is mainly used for aluminum melting, temperature holding of the molten aluminum and ready for casting.
The technological process of producing: 
Aluminum ingot (Raw materials) → 1.25T/time charging system → 5T/h vertical aluminum melting furnace → Launder →12T Round stationary Holding furnace → Temperature increasing, refining, slagging-off → Qualified molten aluminum → Launder → Continuous casting and rolling machine.
II. Main technical parameters and properties of the furnaces 

NO.	Item	5T/h Melting Furnace	12T Holding Furnace	Remark
1	Function	Melt the aluminum ingot	Increasing and preserving the temperature, refining and casting the aluminum liquid
2	Charging capacity	Maх 5T solid materials	Maх 12.8T

3	Depth of molten pool		600mm	600+50
4	Raw materials charging mode	Special charging system	Loading the materials from the furnace door
5	Slag-off mode	Manual	Manual
6	Type of the furnace door	Hinge type 580X340 mm	Hinge type 820X580 mm
7	Aluminum liquid discharging temperature	675-685ºC	720ºC--740ºC	Can be adjusted
8	Maximum operating temperature of the furnace	1000ºC	1000ºC
9	Molten aluminum temperature control accuracy	±5ºC	±5ºC	Manual control
10	Melting speed	Maх 5.5T/h	Temperature increasing speed when full loaded: 20ºC/ h

1.1 The Melting Furnace adopts vertical structure, loading the materials from the top by the tipping bucket feeding machine. When melting, the high-temperature smoke during exhaust would be absorbed by the aluminum ingot in the vertical furnace, which can greatly save the energy;
1.2 Inner diameter of the column is 1350mm, total height is 4500mm, which has three stages. And it can store above 5 Ton aluminum ingot, which could fully absorb the heat of the smoke to lower the energy consumption. Large diameter could guarantee add piles of aluminum ingot smoothly;
1.3 The column of the melting furnace is made up of high intensity phosphate fan-shaped brick (features: strike -resistant, wear-resistant). The using life of the vertical furnace is more than 3 years.
 Structure of vertical furnace 
A. Side wall of bottom furnace is assembled by 8mm steel plate, reinforced with 10# U-bar rib. 
B. Base plate of bottom furnace is assembled by 14mm steel plate, outside extra reinforced with 2pcs ribs. 
C. Side wall of vertical column is assembled by 5mm steel plate, which flanges use 14mm steel plate. 
D. Main exhaust hood is assembled by 5mm steel plate, which fire door uses 5mm steel plate. 
E. Furnace door is assembled by 8mm and 14mm steel plate, which door frame is fabricated by heat-resistant cast iron. 
F. Fume pipe is assembled by 3mm steel plate.

2.1 furnace body steel structure:
The steel structure of the furnace body is completely welded, the shell is made of 8mm thick high quality Q235 steel plate and 16 # i-steel by external strengthening welding, and the bottom of the furnace is made of 16mm thick high quality Q235 steel plate and 20 # i-steel by external strengthening welding, the whole shell forms a net reinforced steel structure, which has good steel strength and air tightness, can fully withstand the mechanical stress and thermal stress of the furnace, all the steel used on the furnace are made of WISCO or Lianyuan steel;
2.2. Furnace Door:
Aluminum alloy ingot and slag are added to 780 * 550 hinge-type furnace door, slot casting is used around the furnace door, high temperature fiber cotton is embedded in the slot to ensure its sealing performance and service life.
2.3 burners: 
12T holding furnaces each equipped with 11.5 million kcal oil-fired high-temperature burners (manual control) .
2.4. Molten pool:
DKS-80 non-stick aluminum castable structure is adopted in the working layer of the heat preservation furnace. Compared with the brick structure, the advantages of this structure are: the non-stick aluminum performance of the working layer is very strong and a small amount of stick aluminum can be scraped off with a picker in the hot state, it will not pollute the molten aluminum alloy, and will not affect the weight of molten aluminum! At the same time, the service life of castable is about 2-3 years longer than that of brick structure
2.5. Description of the combustion system 
Every chamber of the holding furnace adopts 1 set of T86 burner (manual ignition), to ensure the aluminum liquid temperature can be increased to casting temperature quickly under the premise of continuous casting and rolling.
Furnaces for standard configuration, it use manual burner and manual control, customer could choose auto burner depends on own requirement.